RTP Crystal
RbTiOPO4(RTP) crystal is a kind of nonlinear optical crystal material with excellent comprehensive properties. RTP is currently the most commonly used type of practical electro-optic crystals with high frequency repetition, high power and narrow pulse width laser Q switching. RTP electro-optical devices are not only used in laser micromachining and laser ranging, but also in major scientific exploration projects because of their excellent comprehensive performance.
RbTiOPO4(RTP)-a crystal with large nonlinear optical coefficient, large electro-optical coefficient, high photoresist damage threshold and stable physical and chemical properties
The growth temperature ranges from 950 °C to 800 °C and the growth period is usually between 45 and 60 days.As RTP is transparent from 0.4 to 3.5 μm, it can be used in multiple types of laser such as Er:YAG laser at 2.94 μm with fairly good efficiency. Bulk absorption measurements at 1.064 μm range from 50 to 150 ppm using Photothermal Common Path Interferometer.
| Chemical formula | RbTiOPO4 |
| Crystal structure | Orthorhombic |
| Point group | mm2 |
| Lattice parameters, Å | a 12.96 |
| b 10.56 | |
| c 6.49 | |
| Density, g.cm-3 | 3.6 |
| Resistivity (20°C, 20% Humidity), Ohm.cm | 1012 |
| Aperture, mm2 | from 2×2 to 9×9 |
| Length, mm | up to 10 |
| Dimension tolerance | ±0.1 mm |
| Flatness | <l/8 @633 nm |
| Surface quality | Scratch/Dig 10/5 |
| Parallelism | better than 30 arc sec |
| Perpendicularity | better than 30 arc min |
| Angle tolerance | △q < 0.5°, △f < 0.5° |
| Coating | AR coatings |
| Clear aperture | >90% central area |
| Transmitting wavefront distortion | less than l/8 @ 633 nm Dimension |
| Melting Point | ~ 1000 °C |
| Ferroeletric transition temperature | ~810 °C |
| Mohs Hardness | ~5 |
| Thermal Expansion Coefficients, /°C | a1=1.01×10-5, a2=1.37×10-5, a3=-4.17×10-6 |
| Hygroscopic Susceptibility | No |
| Ionic conductivity (room temperature, 10 kHz) | 10-8 S/cm |
| Average refractive index | 1.8 | |
| Transparency range, μm | 0.35 → 4.5 | |
| Residual Absorption (PCI) at 1064 nm | <250 ppm/cm | |
| Electro-optical constants (@ 633 nm, 1 kHz), pm. V-1 | r13 | 10.9 |
| r23 | 15 | |
| r33 | 33 | |
| Dielectric constant | εeff=13 | |
| High damage threshold | >15 J/cm2 at 10 Hz,10 ns at 1064 nm performed on coated crystals of 10 mm long |
| Low operating voltage | 1300 V for Y-cut and 1600 V for X-cut at 1064 nm applied to a crystal pair of 4×4 mm² for the aperture and 2×10 mm for the length |
| Low bulk absorption | <250 ppm/cm at 1064 nm |